Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin BN9003G - Americas - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin BN9003G - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding - Processing Recommendation Extrusion
Any use of this information falls under the rules of our disclaimer.
商品の説明文
NORYL™ BN0039 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This blow moldable grade exhibits a good balance of impact resistance and surface aesthetics. NORYL BN0039 resin, with its Low warpage and dimensional stability, is an excellent candidate for automotive exterior components including spoilers.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 12 cm³/10min ISO 1133
温度 280 °C -
荷重 5 kg -
ASTM数据
メルトフローレイト, MFI 10 g/10min ASTM D 1238
温度 280 °C -
荷重 5 kg -
機械的特性値単位テスト基準
ISO データ
引張弾性率 2170 MPa ISO 527
降伏応力 47 MPa ISO 527
降伏ひずみ 3.4 % ISO 527
破壊応力 42 MPa ISO 527
破壊ひずみ 30.4 % ISO 527
曲げ弾性率 2190 MPa ISO 178
シャルピー衝撃強さ, +23°C N kJ/m² ISO 179/1eU
シャルピー衝撃強さ, -30ﾟC 107 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 26 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC 12 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm N kJ/m² ISO 180/1U
Izod impact strength, -30°C, 4mm 54 kJ/m² ISO 180/1U
ノッチ付きアイゾット衝撃強さ, +23°C, 4mm 25 kJ/m² ISO 180/1A
ノッチ付きアイゾット衝撃強さ, -30°C, 4mm 10 kJ/m² ISO 180/1A
ASTM数据
引張弾性率 2240 MPa ASTM D 638
降伏応力 48 MPa ASTM D 638
破壊応力 42 MPa ASTM D 638
降伏点伸び 3.6 % ASTM D 638
破断伸び 45 % ASTM D 638
曲げ弾性率 2150 MPa ASTM D 790
ノッチ付きIzod衝撃強さ, 1/8 in 320 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, Low-Temperature 127 J/m ASTM D 256
温度 -30 °C -
アイゾット衝撃試験, 1/8 in N J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 110 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 126 °C ISO 75-1/-2
ビカット軟化温度, B 127 °C ISO 306
ビカット軟化温度, 120°C/h 50N 130 °C ISO 306
ASTM数据
DTUL @ 66 psi 124 °C ASTM D 648
DTUL @ 264 psi 108 °C ASTM D 648
ビカット軟化温度 141 °C ASTM D 1525
その他の特性.値単位テスト基準
吸水率. 0.25 % Sim. to ISO 62
吸湿率 0.05 % Sim. to ISO 62
密度. 1060 kg/m³ ISO 1183
密度 1060 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 80 - 85 °C -
Processing Recommendation Extrusion値単位テスト基準
Pre-drying - Temperature 80 - 85 °C -
Pre-drying - Time 2 - 4 h -
樹脂温度 235 - 260 °C -
金型温度 65 - 95 °C -
Zone 1 260 - 225 °C -
Zone 2 230 - 260 °C -
Zone 3 235 - 260 °C -
Zone 4 235 - 260 °C -
Zone 5 235 - 260 °C -
特殊な特性
成形加工法.
ブロー成形.
領域別の利用可能性
北アメリカ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.