Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of MABLEX® 274 - (PC+ABS) - Ravago Group

Material Data Center offers the following functions for MABLEX® 274:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Mablex datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics単位テスト基準
ISO データ
メルトフローレート, MFI 13 g/10min ISO 1133
温度 260 °C -
荷重 5 kg -
成形収縮率, 平行 0.6 % ISO 294-4, 2577
機械的特性単位テスト基準
ISO データ
降伏応力 58 MPa ISO 527
破壊応力 48 MPa ISO 527
破壊ひずみ 52 % ISO 527
曲げ弾性率, 23°C 2400 MPa ISO 178
ノッチ付きIzod衝撃強さ, +23°C 55 kJ/m² ISO 180/1A
ノッチ付きIzod衝撃強さ 30 kJ/m² ISO 180/1A
温度 -30 °C -
熱的特性単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 110 °C ISO 75-1/-2
ビカット軟化温度, A 132 °C ISO 306
ビカット軟化温度, B 124 °C ISO 306
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.6 mm -
厚さhでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 3.2 mm -
燃焼速度, FMVSS, 1mm厚 48 mm/min ISO 3795 (FMVSS 302)
グローワイヤ燃焼性指数 (GWFI) 650 °C IEC 60695-2-12
GWFI - 試験片の厚さ 2 mm -
電気的特性.単位テスト基準
ISO データ
体積抵抗率 1E13 Ohm*m IEC 62631-3-1
表面抵抗率 1E14 Ohm IEC 62631-3-2
耐電圧 24 kV/mm IEC 60243-1
耐トラッキング性 300 - IEC 60112
その他の特性.単位テスト基準
密度. 1130 kg/m³ ISO 1183
Processing Recommendation Injection Molding単位テスト基準
Pre-drying - Temperature 100 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.05 % -
樹脂温度 250 - 270 °C -
金型温度 50 - 80 °C -
Zone 1 225 - 240 °C -
Zone 2 240 - 260 °C -
Zone 3 260 - 270 °C -
Nozzle temperature 250 - 260 °C -
Screw speed 40 - 70 rpm -
Back pressure 0.3 - 1.5 MPa -
後硬化時間 3 - 7 MPa -
特殊な特性
成形加工法.
射出成形.
特殊な特性.
熱安定化.
領域別の利用可能性
ヨーロッパ.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com