Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Luran® S KR2866C - (ASA+PC) - INEOS Styrolution

Material Data Center offers the following functions for Luran® S KR2866C:
unit conversion, PDF datasheet print, comparison with other plastics, application examples, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Luran datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
商品の説明文
Heat-resistant injection-moulding grade with medium toughness for automotive interior and exterior parts as well as housings for electronic goods. Available in Europe only.
Processing/Physical Characteristics単位テスト基準
ISO データ
メルトボリュームレイト, MVR 11 cm³/10min ISO 1133
温度 260 °C -
荷重 5 kg -
成形収縮率, 平行 0.5 % ISO 294-4, 2577
成形収縮率, 直角 0.9 % ISO 294-4, 2577
機械的特性単位テスト基準
ISO データ
引張弾性率 2600 MPa ISO 527
降伏応力 60 MPa ISO 527
降伏ひずみ 3.4 % ISO 527
破壊呼びひずみ 15 % ISO 527
シャルピー衝撃強さ, +23°C N kJ/m² ISO 179/1eU
シャルピー衝撃強さ, -30°C 160 kJ/m² ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C 35 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30°C 5 kJ/m² ISO 179/1eA
熱的特性単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 102 °C ISO 75-1/-2
荷重たわみ温度, 0.45 MPa 113 °C ISO 75-1/-2
ビカット軟化温度, B 110 °C ISO 306
線膨張係数, 平行 90 E-6/K ISO 11359-1/-2
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.6 mm -
電気的特性.単位テスト基準
ISO データ
体積抵抗率 1E12 Ohm*m IEC 62631-3-1
表面抵抗率 1E13 Ohm IEC 62631-3-2
耐電圧 38 kV/mm IEC 60243-1
その他の特性.単位テスト基準
吸水率 0.9 % Sim. to ISO 62
吸湿率 0.25 % Sim. to ISO 62
密度 1110 kg/m³ ISO 1183
試験片の成形条件.単位テスト基準
ISO データ
射出成形, 樹脂温度 280 °C ISO 294
射出成形, 金型温度 80 °C ISO 294
射出成形, 射出速度 200 mm/s ISO 294
Processing Recommendation Injection Molding単位テスト基準
Pre-drying - Temperature 100 °C -
Pre-drying - Time 2 - 4 h -
樹脂温度 260 - 300 °C -
金型温度 40 - 80 °C -
機能
 応力-ひずみ. , Luran® S KR2866C, (ASA+PC), INEOS Styrolution
 割線弾性率−ひずみ. , Luran® S KR2866C, (ASA+PC), INEOS Styrolution
 引張弾性率-温度. , Luran® S KR2866C, (ASA+PC), INEOS Styrolution
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
添加剤.
離型剤.
特殊な特性.
光安定化., 紫外線安定化., 熱安定化.
領域別の利用可能性
その他の情報
村遜速揃
PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 100 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
injection molding, Melt temperature, range: 260 - 300 °C
injection molding, Mold temperature, range: 40 - 80 °C
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.