Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Luran® 388S - SAN - INEOS Styrolution

Check here, which other Luran datasheets, application examples or technical articles are available in Material Data Center

Processing/Physical Characteristics - 機械的特性 - 熱的特性 - 電気的特性. - その他の特性. - 試験片の成形条件. - Processing Recommendation Injection Molding - 機能

Any use of this information falls under the rules of our disclaimer.

商品の説明文

Speciality grade with highest mechanical strength and chemical resistance.

Processing/Physical Characteristics	値	単位	テスト基準
ISO データ
メルトボリュームレイト, MVR	7	cm³/10min	ISO 1133
温度	220	°C	-
荷重	10	kg	-
溶融時の密度	970	kg/m³	-
溶融時の熱伝導率	0.17	W/(m K)	-
溶融時の比熱	2300	J/(kg K)	-
突き出し時の時の温度	99	°C	-

機械的特性	値	単位	テスト基準
ISO データ
引張弾性率	3800	MPa	ISO 527
破壊応力	79	MPa	ISO 527
破壊ひずみ	4	%	ISO 527
引張クリープ弾性率, 1h	3500	MPa	ISO 899-1
引張クリープ弾性率, 1000h	2800	MPa	ISO 899-1
シャルピー衝撃強さ, +23°C	21	kJ/m²	ISO 179/1eU
シャルピー衝撃強さ, -30°C	19	kJ/m²	ISO 179/1eU
ノッチ付きシャルピー衝撃強さ, +23°C	2.5	kJ/m²	ISO 179/1eA

熱的特性	値	単位	テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa	90	°C	ISO 75-1/-2
荷重たわみ温度, 0.45 MPa	102	°C	ISO 75-1/-2
ビカット軟化温度, B	107	°C	ISO 306
線膨張係数, 平行	70	E-6/K	ISO 11359-1/-2
1.5mm厚さでの燃焼性	HB	class	IEC 60695-11-10
試験片の厚さ	1.6	mm	-
Yellow Card 可用	はい	-	-
酸素指数	18	%	ISO 4589-1/-2

電気的特性.	値	単位	テスト基準
ISO データ
比誘電率, 100Hz	3	-	IEC 62631-2-1
比誘電率, 1MHz	2.8	-	IEC 62631-2-1
誘電正接, 100Hz	50	E-4	IEC 62631-2-1
誘電正接, 1MHz	80	E-4	IEC 62631-2-1
体積抵抗率	>1E13	Ohm*m	IEC 62631-3-1
表面抵抗率	>1E15	Ohm	IEC 62631-3-2
耐トラッキング性	475	-	IEC 60112

その他の特性.	値	単位	テスト基準
吸湿率	0.3	%	Sim. to ISO 62
密度	1080	kg/m³	ISO 1183

試験片の成形条件.	値	単位	テスト基準
ISO データ
射出成形, 樹脂温度	250	°C	ISO 294
射出成形, 金型温度	60	°C	ISO 294
射出成形, 射出速度	200	mm/s	ISO 294

Processing Recommendation Injection Molding	値	単位	テスト基準
Pre-drying - Temperature	80	°C	-
Pre-drying - Time	2 - 4	h	-
樹脂温度	220 - 260	°C	-
金型温度	40 - 80	°C	-

機能

特殊な特性

成形加工法.

射出成形., 異形押出成形., シート押出成形., その他の押出成形., 熱成形.

納入形状.

ペレット.

特殊な特性.

透明.

領域別の利用可能性

北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ

その他の情報

村遜速揃

PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
injection molding, Melt temperature, range: 220 - 260 °C
injection molding, Melt temperature, recommended: 250 °C
injection molding, Mold temperature, range: 40 - 80 °C
injection molding, Mold temperature, recommended: 60 °C

その他の押出成形.

PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
Extrusion, Prepreg, Melt temperature: 220 - 240 °C
Extrusion, Pipes, Melt temperature: 220 - 240 °C

族臓遜造揃

PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
Extrusion, Profiles, Melt temperature: 240 °C

促揃臓村促速揃

PREPROCESSING
Pre/Post-processing, Pre-drying, Temperature: 80 °C
Pre/Post-processing, Pre-drying, Time: 2 - 4 h

PROCESSING
Extrusion, Plates, Melt temperature: 220 - 240 °C

耐薬品性

酸
	5wt％酢酸 (23ﾟC)
	10wt％クエン酸 (23ﾟC)
	10wt％乳酸 (23ﾟC)
	36wt％塩酸 (23ﾟC)
	40wt％硝酸 (23ﾟC)
	38wt％硫酸 (23ﾟC)
	5wt％硫酸 (23ﾟC)
	40wt％硝酸 (23ﾟC)
塩基
	35wt％水酸化ナトリウム (23ﾟC)
	1wt％水酸化ナトリウム (23ﾟC)
	10wt％水酸化アンモニウム (23ﾟC)
アルコール
	イソプロピルアルコール23℃ (23ﾟC)
	メタノール　23℃ (23ﾟC)
	エタノール　23℃ (23ﾟC)
炭化水素
	ヘキサン (23ﾟC)
	トルエン (23ﾟC)
	イソオクタン (23ﾟC)
ケトン系溶剤
	アセトン (23ﾟC)
エーテル溶剤
	ジエチルエーテル (23ﾟC)
標準燃料
	ディーゼル燃料（ISO 1817液F) (23ﾟC)
食塩水
	10wt％塩化ナトリウム (23ﾟC)
	10wt％次亜塩素酸ナトリウム (23ﾟC)
	20wt％炭酸ナトリウム (23ﾟC)
	2wt％炭酸ナトリウム (23ﾟC)
	50wt％ジンクロメート (23ﾟC)
その他
	エチルアセテート (23ﾟC)
	過酸化水素 (23ﾟC)
	1wt%ノニルフェノキシ-ポリエチレノキシ-エタノール水... (23ﾟC)
	水 (23ﾟC)

Disclaimer

Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.

Created: Source: www.materialdatacenter.com