Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of KIBILAC PW-978B - ASA - Chi Mei Corporation

Material Data Center offers the following functions for KIBILAC PW-978B:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Kibilac datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 機械的特性 - 熱的特性 - その他の特性. - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトボリュームレイト, MVR 12 cm³/10min ISO 1133
温度 220 °C -
荷重 10 kg -
成形収縮率, 平行 0.6 % ISO 294-4, 2577
ASTM数据
メルトフローレイト, MFI 13 g/10min ASTM D 1238
温度 220 °C -
荷重 10 kg -
機械的特性値単位テスト基準
ISO データ
降伏応力 47 MPa ISO 527
破壊応力 34 MPa ISO 527
曲げ弾性率, 23°C 2100 MPa ISO 178
曲げ強さ 67 MPa ISO 178
ノッチ付きシャルピー衝撃強さ, +23°C 12.3 kJ/m² ISO 179/1eA
ノッチ付きシャルピー衝撃強さ, -30ﾟC 6 kJ/m² ISO 179/1eA
ノッチ付きIzod衝撃強さ, +23°C 12 kJ/m² ISO 180/1A
ノッチ付きIzod衝撃強さ 5 kJ/m² ISO 180/1A
温度 -30 °C -
ASTM数据
降伏応力 46 MPa ASTM D 638
曲げ弾性率 2256 MPa ASTM D 790
曲げ強さ 66.3 MPa ASTM D 790
ロックウェル硬度 R 105 - ASTM D 785
ノッチ付きIzod衝撃強さ, 1/8 in 203 J/m ASTM D 256
ノッチ付きIzod衝撃強さ, 1/4 in 192 J/m ASTM D 256
熱的特性値単位テスト基準
ISO データ
荷重たわみ温度, 1.80 MPa 83 °C ISO 75-1/-2
ビカット軟化温度, A 112 °C ISO 306
ビカット軟化温度, B 100 °C ISO 306
線膨張係数, 平行 91 E-6/K ISO 11359-1/-2
1.5mm厚さでの燃焼性 HB class IEC 60695-11-10
試験片の厚さ 1.5 mm -
ASTM数据
UL94 燃焼性 HB - UL 94
追加試験片の厚さ 1.59 mm -
ビカット軟化温度 113 °C ASTM D 1525
その他の特性.値単位テスト基準
密度. 1070 kg/m³ ISO 1183
密度 1070 kg/m³ ASTM D 792
Processing Recommendation Injection Molding値単位テスト基準
Pre-drying - Temperature 90 - 95 °C -
Pre-drying - Time 3 h -
金型温度 40 - 80 °C -
Feed temperature 230 - 250 °C -
Zone 1 240 - 260 °C -
Nozzle temperature 240 - 260 °C -
Injection pressure 5 - 7 MPa -
Back pressure 0.5 - 1.5 MPa -
後硬化時間 4 - 6 MPa -
特殊な特性
成形加工法.
射出成形.
納入形状.
ペレット.
特殊な特性.
高耐衝撃及び耐衝撃改良., 熱安定化.
Certifications
RoHS
アプリケーション
自動車, 電気電子
領域別の利用可能性
アジア/太平洋地域.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.