Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.
This is the free Material Data Center Datasheet of HOSTAFORM® C 2521 - POM - Celanese
Material Data Center offers the following functions for HOSTAFORM® C 2521:
unit conversion, PDF datasheet print, comparison with other plastics, application examples, snap fit calculation, beam deflection calculation, cooling time calculation, CAE Interfaces
unit conversion, PDF datasheet print, comparison with other plastics, application examples, snap fit calculation, beam deflection calculation, cooling time calculation, CAE Interfaces
Check here, which other Hostaform datasheets, application examples or technical articles are available in Material Data Center
Use the following short links to get directly to the properties of interest in this datasheet:
商品の説明文
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 29988- POM-K, M-GNR, 01-002
POM copolymer
Stiff-flowing type for injection molding and extrusion with high impact toughness and good tracking resistance over a high range of temperature; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
Ranges of applications: injection molding thick-walled, void-free molded parts; extrusion e.g. for boards and pipes.
FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Molding compound ISO 29988- POM-K, M-GNR, 01-002
POM copolymer
Stiff-flowing type for injection molding and extrusion with high impact toughness and good tracking resistance over a high range of temperature; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
Ranges of applications: injection molding thick-walled, void-free molded parts; extrusion e.g. for boards and pipes.
FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
| Flammability @1.6mm nom. thickn. | HB | - |
| Flammability at thickness h (3 mm) | HB | UL recognition (h) |
| Processing/Physical Characteristics | 値 | 単位 | テスト基準 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ISO データ | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| メルトボリュームレイト, MVR | 2.5 | cm³/10min | ISO 1133 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 温度 | 190 | °C | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 荷重 | 2.16 | kg | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 成形収縮率, 平行 | 2.1 | % | ISO 294-4, 2577 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 成形収縮率, 直角 | 1.8 | % | ISO 294-4, 2577 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 溶融時の密度 | 1200 | kg/m³ | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 溶融時の熱伝導率 | 0.155 | W/(m K) | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 溶融時の比熱 | 2210 | J/(kg K) | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 突き出し時の時の温度 | 140 | °C | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 機械的特性 | 値 | 単位 | テスト基準 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ISO データ | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 引張弾性率 | 2600 | MPa | ISO 527 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 降伏応力 | 62 | MPa | ISO 527 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 降伏ひずみ | 9 | % | ISO 527 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 破壊呼びひずみ | 32 | % | ISO 527 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| シャルピー衝撃強さ, +23°C | 250 | kJ/m² | ISO 179/1eU | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| シャルピー衝撃強さ, -30°C | 250 | kJ/m² | ISO 179/1eU | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ノッチ付きシャルピー衝撃強さ, +23°C | 8.5 | kJ/m² | ISO 179/1eA | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ノッチ付きシャルピー衝撃強さ, -30°C | 7 | kJ/m² | ISO 179/1eA | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 熱的特性 | 値 | 単位 | テスト基準 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ISO データ | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 溶融温度, 10°C/min | 165 | °C | ISO 11357-1/-3 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 荷重たわみ温度, 1.80 MPa | 101 | °C | ISO 75-1/-2 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 線膨張係数, 平行 | 110 | E-6/K | ISO 11359-1/-2 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 1.5mm厚さでの燃焼性 | HB | class | IEC 60695-11-10 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 試験片の厚さ | 1.5 | mm | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 厚さhでの燃焼性 | HB | class | IEC 60695-11-10 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 試験片の厚さ | 3.0 | mm | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Yellow Card 可用 | はい | - | - | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 電気的特性. | 値 | 単位 | テスト基準 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ISO データ | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 比誘電率, 100Hz | 4 | - | IEC 62631-2-1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 比誘電率, 1MHz | 4 | - | IEC 62631-2-1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 誘電正接, 100Hz | 15 | E-4 | IEC 62631-2-1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 誘電正接, 1MHz | 50 | E-4 | IEC 62631-2-1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 体積抵抗率 | 1E12 | Ohm*m | IEC 62631-3-1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 表面抵抗率 | 1E14 | Ohm | IEC 62631-3-2 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 耐電圧 | 35 | kV/mm | IEC 60243-1 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| その他の特性. | 値 | 単位 | テスト基準 |
| 吸水率 | 0.65 | % | Sim. to ISO 62 |
| 吸湿率 | 0.2 | % | Sim. to ISO 62 |
| 密度 | 1410 | kg/m³ | ISO 1183 |
特殊な特性
成形加工法.
射出成形., フィルム押出成形., 異形押出成形., シート押出成形., その他の押出成形., ブロー成形.
納入形状.
ペレット.
添加剤.
離型剤.
な特性
Thermal Stability, Copolymer
耐薬品性
Alkali Resistance, Solvent Resistance, Oxidation Resistance
Certifications
Food contact, Food approval 10/2011, Food approval FDA 21 CFR, Drinking water contact
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ
その他の情報
村遜速揃
General drying is not necessary due to low moisture absorption of
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard injection moulding machines with three phase (15 to 25 D)
plasticating screws will fit.
Conditioning e.g. moisturizing is not necessary.
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard injection moulding machines with three phase (15 to 25 D)
plasticating screws will fit.
Conditioning e.g. moisturizing is not necessary.
フィルム押出成形.
General drying is not necessary due to low moisture absorption of
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
その他の押出成形.
General drying is not necessary due to low moisture absorption of
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
族臓遜造揃
General drying is not necessary due to low moisture absorption of
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
促揃臓村促速揃
General drying is not necessary due to low moisture absorption of
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with grooved feed zone and short compression
screws (minimum 25 D) will fit.
Melt temperature 180-190 °C
Conditioning e.g. moisturizing is not necessary.
In case of very thick wall thickness profiles after-annealing it is
recommended to reduce internal stress.
Annealing temperature 130-140 °C
Annealing time 10 min/mm thickness
促促鱈臓村速揃
General drying is not necessary due to low moisture absorption of
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with plasticating screws (20 to 25 D) will fit.
Melt temperature 180-190 °C
Mould-surface temperature 60-100 °C
Conditioning e.g. moisturizing is not necessary.
the resin.
In case of bad storage conditions (water contact or condensed water)
the use of a recirculating air dryer (100 to 120 °C / max. 40 mm
layer / 3 to 6 hours) is recommended.
Max. Water content 0,2 %
Standard extruders with plasticating screws (20 to 25 D) will fit.
Melt temperature 180-190 °C
Mould-surface temperature 60-100 °C
Conditioning e.g. moisturizing is not necessary.
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com
Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.
Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.