Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox. Information about Biopolymers, a project by FH Hannover and M-Base Engineering & Software GmbH sponsored by Fachagentur Nachwachsende Rohstoffe (FNR).

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Bio-Flex® F 2101 - PLA... - FKuR Kunststoff GmbH

Material Data Center offers the following functions for Bio-Flex® F 2101:
unit conversion, PDF datasheet print, comparison with other plastics

Check here, which other Bio-Flex datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - 熱的特性 - その他の特性. - 機械的特性(ィルム) - Processing Recommendation Extrusion
Any use of this information falls under the rules of our disclaimer.
商品の説明文
Biodegradable compound for blown film extrusion. Used in applications such as fruit bags and T-shirt bags.
Processing/Physical Characteristics値単位テスト基準
ISO データ
メルトフローレート, MFI 4.5 g/10min ISO 1133
温度 190 °C -
荷重 2.16 kg -
熱的特性値単位テスト基準
ISO データ
溶融温度, 10ﾟC/min 155 °C ISO 11357-1/-3
その他の特性.値単位テスト基準
密度. 1230 kg/m³ ISO 1183
機械的特性(ィルム)値単位テスト基準
ISO データ
引張弾性率, 平行 505 MPa ISO 527-3
引張弾性率, 直角 155 MPa ISO 527-3
降伏ひずみ, 平行 270 % ISO 527-3
降伏ひずみ, n直角 400 % ISO 527-3
破壊応力, 平行 31 MPa ISO 527-3
破壊応力, 直角 31 MPa ISO 527-3
最大ひずみ, 平行 270 % ISO 527-3
最大ひずみ, 直角 400 % ISO 527-3
押出成形のタイプ. blown - -
試験片の厚さ. 0.025 mm -
Processing Recommendation Extrusion値単位テスト基準
Type of extrusion blown - -
Pre-drying - Temperature 60 °C -
Pre-drying - Time 2 - 4 h -
樹脂温度 <190 °C -
Feed temperature 40 - 60 °C -
Zone 1 160 °C -
Zone 2 165 °C -
Zone 3 170 °C -
Zone 4 175 °C -
Nozzle temperature 180 °C -
特殊な特性
成形加工法.
Blown Film Extrusion, フィルム押出成形.
納入形状.
ペレット.
Certifications
Contains renewable resources, Biodegradable, Food contact
アプリケーション
パッケージング, おもちゃ
領域別の利用可能性
北アメリカ., ヨーロッパ., アジア/太平洋地域., 南・中央アメリカ., 近東/アフリカ
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.