Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of Rynite® 530HTE NC010 - PET-GF30 - DuPont Engineering Polymers

Material Data Center offers the following functions for Rynite® 530HTE NC010:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation

Check here, which other Rynite datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
Product Texts

Common features of Rynite® thermoplastic polyester include mechanical and physical properties such as excellent balance of strength and stiffness, dimensional stability, creep resistance, heat resistance, high surface gloss and good inherent electrical properties at elevated temperature. It can be processed over a broad temperature range and has excellent flow properties.

Rynite® thermoplastic polyester resins are typically used in demanding applications in the automotive, electrical and electronics, appliances where they successfully replace metals and thermosets, as well as other thermoplastic polymers. 

 

Rynite® 530HTE NC010 is a 30% glass reinforced modified polyethylene terephthalate resin with excellent high temperature dielectric properties.

Processing/Physical CharacteristicsValueUnitTest Standard
ASTM Data
Mold Shrinkage, MD 0.001 mm/mm ASTM D 955
Mold Shrinkage, TD 0.007 mm/mm ASTM D 955
Density, 73°F 1580 kg/m³ ASTM D 792
Water Absorption, 24hr 0.06 % ASTM D 570
Rheological propertiesValueUnitTest Standard
CAMPUS/ISO Data
Melt volume-flow rate, MVR 9 cm³/10min ISO 1133
Temperature 280 °C ISO 1133
Load 2.16 kg ISO 1133
Molding shrinkage, parallel 0.1 % ISO 294-4, 2577
Molding shrinkage, normal 0.6 % ISO 294-4, 2577
Mechanical propertiesValueUnitTest Standard
CAMPUS/ISO Data
Tensile Modulus 11000 MPa ISO 527-1/-2
Stress at break 170 MPa ISO 527-1/-2
Strain at break 2.3 % ISO 527-1/-2
ASTM Data
Tensile Modulus 10700 MPa ASTM D 638
Tensile Strength 169 MPa ASTM D 638
Elongation at Break 2.3 % ASTM D 638
Compressive Strength 241 MPa ASTM D 695
Flexural Modulus 8960 MPa ASTM D 790
Flexural Strength 240 MPa ASTM D 790
Rockwell Hardness R 120 - ASTM D 785
Izod Impact notched, 1/8 in 0.09 kJ/m ASTM D 256
Izod Impact notched, Low-Temperature 0.085 kJ/m ASTM D 256
Temperature -40 °C ASTM D 256
Thermal propertiesValueUnitTest Standard
CAMPUS/ISO Data
Melting temperature, 10°C/min 252 °C ISO 11357-1/-3
Burning Behav. at thickness h HB class IEC 60695-11-10
Thickness tested 0.8 mm IEC 60695-11-10
UL recognition UL - -
ASTM Data
UL 94 Flame rating HB - UL 94
Thickness tested 1.5 mm -
DTUL @ 66 psi 251 °C ASTM D 648
DTUL @ 264 psi 233 °C ASTM D 648
Electrical propertiesValueUnitTest Standard
CAMPUS/ISO Data
Volume resistivity >1E13 Ohm*m IEC 60093
Electric strength 34 kV/mm IEC 60243-1
ASTM Data
Dielectric Strength, Short Time 21.5 kV/mm ASTM D 149
Dissipation Factor, 1 MHz 0.014 - ASTM D 150
Dielectric Constant, 1 MHz 4.1 - ASTM D 150
Surface Resistivity 1E13 Ohm ASTM D 257
Volume Resistivity 1E15 Ohm*cm ASTM D 257
Rheological calculation propertiesValueUnitTest Standard
CAMPUS/ISO Data
Ejection temperature 170 °C -
Characteristics
Processing
Injection Molding
Delivery form
Pellets, Natural Color
Special Characteristics
Heat stabilized or stable to heat
Applications
Electrical and Electronical
Regional Availability
Other text information
Injection molding
Molding guide
When lower mold temperatures are used, the initial warpage and shrinkage will be lower, but the surface appearance will be poorer and the dimensional change may be greater when parts are subsequently heated.
Disclaimer
Copyright M-Base Engineering+Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from M-Base; this is especially valid for claims of compensation resulting from consequential damages. M-Base explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: 2015-09-04 Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.