Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin PX0844 - Americas - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin PX0844 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
NORYL™ PX0844 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This grade exhibits very low moisture absorption, hydrolytic stability, dimensional stabilty, good foam adhesion, and property retention over a wide temperature range. NORYL PX0844 resin is inherently UL94 HB and is an excellent candidate for automotive interior applications such as instrument panels, audio components, speaker housings, and interior trim. *see NORYL PX0888 resin for higher heat resistance.
Processing/Physical CharacteristicsValueUnitTest Standard
ASTM Data
Melt Flow Index, MFI 13.7 g/10min ASTM D 1238
Temperature 280 °C -
Load 5 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 2350 MPa ISO 527
Yield stress 47 MPa ISO 527
Yield strain 2.9 % ISO 527
Stress at break 43 MPa ISO 527
Strain at break 43 % ISO 527
Flexural modulus 2400 MPa ISO 178
Flexural strength 78 MPa ISO 178
Izod notched impact strength, +23°C, 4mm 17 kJ/m² ISO 180/1A
Izod notched impact strength, -30°C, 4mm 10 kJ/m² ISO 180/1A
ASTM Data
Tensile Modulus 2290 MPa ASTM D 638
Tensile Strength at Yield 49 MPa ASTM D 638
Tensile Strength at Break 44 MPa ASTM D 638
Elongation at Yield 3 % ASTM D 638
Elongation at Break 30 % ASTM D 638
Flexural Modulus 2550 MPa ASTM D 790
Rockwell Hardness R 114 - ASTM D 785
Izod Impact notched, 1/8 in 234 J/m ASTM D 256
Izod Impact notched, Low-Temperature 133 J/m ASTM D 256
Temperature -40 °C -
Thermal propertiesValueUnitTest Standard
ISO Data
Vicat softening temperature, B 125 °C ISO 306
Vicat softening temperature, 120°C/h 50N 128 °C ISO 306
ASTM Data
DTUL @ 66 psi 120 °C ASTM D 648
DTUL @ 264 psi 105 °C ASTM D 648
Other propertiesValueUnitTest Standard
Density 1060 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 105 - 110 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤0.02 % -
Melt temperature 275 - 305 °C -
Mold temperature 70 - 100 °C -
Zone 1 245 - 295 °C -
Zone 2 255 - 300 °C -
Zone 3 265 - 305 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
Characteristics
Processing
Injection Molding
Chemical Resistance
Hydrolytically Stable
Applications
Automotive
Regional Availability
North America
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.