Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL™ Resin N850 - Europe - (PPE+PS) - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL™ Resin N850 - Europe:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
NORYL™ N850 resin is a non-reinforced blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS). This high flow, injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of 5VA at 3mm and V0 at 1.5mm along with UL746C Outdoor Suitability rating of F2. NORYL N850 resin exhibits high impact strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for electrical and business equipment applications.
Processing/Physical CharacteristicsValueUnitTest Standard
ASTM Data
Melt Flow Index, MFI 18 g/10min ASTM D 1238
Temperature 260 °C -
Load 3.8 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 2950 MPa ISO 527
Yield stress 66 MPa ISO 527
Yield strain 3.2 % ISO 527
Stress at break 61 MPa ISO 527
Strain at break 4.5 % ISO 527
Flexural modulus 2600 MPa ISO 178
Izod notched impact strength, +23°C, 4mm 10 kJ/m² ISO 180/1A
ASTM Data
Tensile Modulus 2620 MPa ASTM D 638
Tensile Strength at Yield 62 MPa ASTM D 638
Tensile Strength at Break 48 MPa ASTM D 638
Elongation at Yield 3.6 % ASTM D 638
Elongation at Break 18 % ASTM D 638
Flexural Modulus 2410 MPa ASTM D 790
Izod Impact notched, 1/8 in 213 J/m ASTM D 256
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 82 °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 95 °C ISO 75-1/-2
Vicat softening temperature, 120°C/h 50N 108 °C ISO 306
Burning behav. at 1.5 mm nom. thickn. V-0 class IEC 60695-11-10
Thickness tested 1.5 mm -
Burning behav. at thickness h HB class IEC 60695-11-10
Thickness tested 1.0 mm -
Burning behav. 5V at thickness h 5VA class IEC 60695-11-20
Thickness tested 3.0 mm -
ASTM Data
DTUL @ 66 psi 93 °C ASTM D 648
DTUL @ 264 psi 82 °C ASTM D 648
Vicat Temperature 101 °C ASTM D 1525
Other propertiesValueUnitTest Standard
Density 1130 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 75 - 80 °C -
Pre-drying - Time 3 - 4 h -
Processing humidity ≤-0.02 % -
Melt temperature 250 - 275 °C -
Mold temperature 55 - 75 °C -
Zone 1 215 - 265 °C -
Zone 2 225 - 270 °C -
Zone 3 240 - 275 °C -
Screw speed 20 - 100 rpm -
Back pressure 0.3 - 0.7 MPa -
Characteristics
Processing
Injection Molding
Additives
Flame retarding agent
Special Characteristics
Flame retardant
Chemical Resistance
Hydrolytically Stable
Regional Availability
Europe
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.