Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LUPOY HI5007U - (PC+ABS) - LG Chem

Material Data Center offers the following functions for LUPOY HI5007U:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lupoy datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Any use of this information falls under the rules of our disclaimer.
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt flow index, MFI 14 g/10min ISO 1133
Temperature 260 °C -
Load 5 kg -
Molding shrinkage, parallel 0.7 % ISO 294-4, 2577
Molding shrinkage, normal 0.7 % ISO 294-4, 2577
ASTM Data
Melt Flow Index, MFI 3.7 g/10min ASTM D 1238
Temperature 250 °C -
Load 2.16 kg -
Mold Shrinkage, MD 0.007 mm/mm ASTM D 955
Mold Shrinkage, TD 0.007 mm/mm ASTM D 955
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 1800 MPa ISO 527
Yield stress 50 MPa ISO 527
Yield strain 4.3 % ISO 527
Stress at break 54 MPa ISO 527
Strain at break 120 % ISO 527
Flexural modulus, 23°C 2180 MPa ISO 178
Flexural strength 75 MPa ISO 178
Charpy notched impact strength, +23°C 59[1] kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C 33[1] kJ/m² ISO 179/1eA
Izod notched impact strength, +23°C 55[1] kJ/m² ISO 180/1A
Izod notched impact strength 18[1] kJ/m² ISO 180/1A
Temperature -40 °C -
Rockwell hardness R 115 - ISO 2039-2
ASTM Data
Tensile Modulus 2178 MPa ASTM D 638
Tensile Strength at Yield 54 MPa ASTM D 638
Tensile Strength at Break 51 MPa ASTM D 638
Elongation at Yield 4.5 % ASTM D 638
Elongation at Break 126 % ASTM D 638
Flexural Modulus 2083 MPa ASTM D 790
Flexural Strength 87.3 MPa ASTM D 790
Rockwell Hardness R 115 - ASTM D 785
Izod Impact notched, 1/8 in 627 J/m ASTM D 256
Izod Impact notched, 1/4 in 471 J/m ASTM D 256
Izod Impact notched, Low-Temperature 255 J/m ASTM D 256
Temperature -30 °C -
1: 4 mm
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 94[2] °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 117[2] °C ISO 75-1/-2
Vicat softening temperature, B 113 °C ISO 306
Coeff. of linear therm. expansion, parallel 78 E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion, normal 81 E-6/K ISO 11359-1/-2
ASTM Data
Coefficient of Thermal Expansion, MD 78 E-6/K ASTM D 696
Coefficient of Thermal Expansion, TD 81 E-6/K ASTM D 696
DTUL @ 66 psi 124 °C ASTM D 648
DTUL @ 264 psi 105 °C ASTM D 648
Vicat Temperature 117 °C ASTM D 1525
2: 4 mm
Electrical propertiesValueUnitTest Standard
ISO Data
Volume resistivity 1E15 Ohm*m IEC 62631-3-1
Surface resistivity 1E15 Ohm IEC 62631-3-2
ASTM Data
Dielectric Strength, Short Time 25 kV/mm ASTM D 149
Surface Resistivity 1E15 Ohm ASTM D 257
Volume Resistivity 1E17 Ohm*cm ASTM D 257
Other propertiesValueUnitTest Standard
Humidity absorption 0.2 % Sim. to ISO 62
Density 1130 kg/m³ ISO 1183
Density 1130 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 80 - 100 °C -
Pre-drying - Time 4 - 6 h -
Processing humidity ≤0.02 % -
Melt temperature 240 - 260 °C -
Mold temperature 60 - 80 °C -
Zone 1 240 - 260 °C -
Zone 2 250 - 270 °C -
Zone 3 250 - 270 °C -
Nozzle temperature 250 - 280 °C -
Characteristics
Processing
Injection Molding
Applications
Automotive, Electrical and Electronical, General Purpose
Regional Availability
North America, Europe, Asia Pacific, South and Central America
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com