Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer HFD1034 - Americas - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer HFD1034 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
7 MFR LEXAN HFD Copolymer UV-stabilized, available in transparent colors only

UL Yellow Card Link E121562-100987584
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt volume-flow rate, MVR 6 cm³/10min ISO 1133
Temperature 300 °C -
Load 1.2 kg -
ASTM Data
Melt Flow Index, MFI 7 g/10min ASTM D 1238
Temperature 300 °C -
Load 1.2 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 2080 MPa ISO 527
Yield stress 60 MPa ISO 527
Yield strain 6 % ISO 527
Stress at break 73 MPa ISO 527
Strain at break 50 % ISO 527
Flexural modulus 2070 MPa ISO 178
Charpy impact strength, +23°C, 3mm N kJ/m² ISO 179/1eU
Charpy impact strength, -30°C, 3mm N kJ/m² ISO 179/1eU
Charpy notched impact strength, +23°C, 3mm 82 kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C, 3mm 69 kJ/m² ISO 179/1eA
Izod impact strength, +23°C N kJ/m² ISO 180/1U
Izod notched impact strength, +23°C, 3mm 72 kJ/m² ISO 180/1A
Izod notched impact strength, -30°C, 3mm 63 kJ/m² ISO 180/1A
ASTM Data
Tensile Modulus 2260 MPa ASTM D 638
Tensile Strength at Yield 58 MPa ASTM D 638
Tensile Strength at Break 67 MPa ASTM D 638
Elongation at Yield 6 % ASTM D 638
Elongation at Break 142 % ASTM D 638
Flexural Modulus 2240 MPa ASTM D 790
Rockwell Hardness R 120 - ASTM D 785
Izod Impact notched, 1/8 in 966 J/m ASTM D 256
Izod Impact notched, Low-Temperature 899 J/m ASTM D 256
Temperature -30 °C -
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 115 °C ISO 75-1/-2
Vicat softening temperature, B 130 °C ISO 306
Vicat softening temperature, 120°C/h 50N 131 °C ISO 306
Burning behav. at thickness h HB class IEC 60695-11-10
Thickness tested 0.8 mm -
ASTM Data
DTUL @ 66 psi 125 °C ASTM D 648
DTUL @ 264 psi 115 °C ASTM D 648
Vicat Temperature 136 °C ASTM D 1525
Other propertiesValueUnitTest Standard
Water absorption 0.3 % Sim. to ISO 62
Humidity absorption 0.15 % Sim. to ISO 62
Density 1200 kg/m³ ISO 1183
Density 1200 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 105 - 110 °C -
Pre-drying - Time 3 - 4 h -
Melt temperature 260 - 305 °C -
Mold temperature 50 - 80 °C -
Zone 1 240 - 280 °C -
Zone 2 250 - 295 °C -
Zone 3 260 - 305 °C -
Screw speed 35 - 75 rpm -
Back pressure 0.3 - 0.7 MPa -
Characteristics
Processing
Injection Molding
Special Characteristics
Transparent
Regional Availability
North America
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.