Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of LEXAN™ Copolymer FST9405 - Americas - PC - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for LEXAN™ Copolymer FST9405 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Lexan datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Processing/Physical Characteristics - Mechanical properties - Thermal properties - Other properties - Processing Recommendation Injection Molding
Any use of this information falls under the rules of our disclaimer.
Product Texts
LEXAN FST9405 resin is a high flow PC Copolymer Resin, suitable for injection molding. This halogen-free flame retardant resin is OSU55/55 and FAR25.853 compliant and an ideal candidate for aircraft interior applications. Available in opaque colors.
Processing/Physical CharacteristicsValueUnitTest Standard
ISO Data
Melt volume-flow rate, MVR 10 cm³/10min ISO 1133
Temperature 300 °C -
Load 1.2 kg -
ASTM Data
Melt Flow Index, MFI 9 g/10min ASTM D 1238
Temperature 300 °C -
Load 1.2 kg -
Mechanical propertiesValueUnitTest Standard
ISO Data
Tensile Modulus 2600 MPa ISO 527
Yield stress 77 MPa ISO 527
Yield strain 6 % ISO 527
Stress at break 70 MPa ISO 527
Strain at break 50 % ISO 527
Flexural modulus 2500 MPa ISO 178
Charpy impact strength, +23°C N kJ/m² ISO 179/1eU
Charpy impact strength, -30°C N kJ/m² ISO 179/1eU
Charpy impact strength, +23°C, 3mm N kJ/m² ISO 179/1eU
Charpy impact strength, -30°C, 3mm N kJ/m² ISO 179/1eU
Charpy notched impact strength, +23°C N kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C N kJ/m² ISO 179/1eA
Charpy notched impact strength, +23°C, 3mm N kJ/m² ISO 179/1eA
Charpy notched impact strength, -30°C, 3mm N kJ/m² ISO 179/1eA
Izod impact strength, +23°C N kJ/m² ISO 180/1U
Izod notched impact strength, +23°C, 4mm 11 kJ/m² ISO 180/1A
Izod notched impact strength, -30°C, 4mm 9 kJ/m² ISO 180/1A
Izod notched impact strength, +23°C, 3mm 12 kJ/m² ISO 180/1A
ASTM Data
Tensile Modulus 2600 MPa ASTM D 638
Tensile Strength at Yield 77 MPa ASTM D 638
Tensile Strength at Break 70 MPa ASTM D 638
Elongation at Yield 6 % ASTM D 638
Elongation at Break 75 % ASTM D 638
Flexural Modulus 2700 MPa ASTM D 790
Izod Impact notched, 1/8 in 130 J/m ASTM D 256
Izod Impact notched, Low-Temperature 85 J/m ASTM D 256
Temperature -30 °C -
Thermal propertiesValueUnitTest Standard
ISO Data
Temp. of deflection under load, 1.80 MPa 94 °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 104 °C ISO 75-1/-2
Vicat softening temperature, 120°C/h 50N 113 °C ISO 306
ASTM Data
DTUL @ 66 psi 105 °C ASTM D 648
DTUL @ 264 psi 95 °C ASTM D 648
Vicat Temperature 114 °C ASTM D 1525
Other propertiesValueUnitTest Standard
Density 1330 kg/m³ ISO 1183
Density 1330 kg/m³ ASTM D 792
Processing Recommendation Injection MoldingValueUnitTest Standard
Pre-drying - Temperature 95 - 100 °C -
Pre-drying - Time 6 - 8 h -
Melt temperature 250 - 280 °C -
Mold temperature 50 - 80 °C -
Zone 1 230 - 250 °C -
Zone 2 240 - 270 °C -
Zone 3 250 - 280 °C -
Screw speed 40 - 70 rpm -
Back pressure 0.3 - 0.7 MPa -
Characteristics
Processing
Injection Molding
Additives
Flame retarding agent
Special Characteristics
Flame retardant
Applications
Automotive
Regional Availability
North America
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com